ON SEPTEMBER 5, 2004, MR. ROBERT GALENTY OF ISELIN, NJ, PETITIONED THE AGENCY TO CONDUCT DEFECT INVESTIGATIONS OF CERTAIN MODEL YEAR (MY) 1993-1997 VEHICLES PRODUCED BY DAIMLERCHRYSLER CORPORATION.HIS PETITION IDENTIFIED THREE ISSUES OF CONCERN: 1) FUEL LEAKING FROM THE FUEL INJECTOR RAILS; 2) BRAKE FLUID CONTAMINATION RESULTING IN BRAKE FAILURE; AND 3) SUSCEPTIBILITY OF THE VEHICLE FRAME TO DAMAGE WHILE THE VEHICLE IS BEING TOWED.MR. GALANTY ALLEGED THAT HIS 1996 DODGE INTREPID HAD EACH OF THESE THREE PROBLEMS.CONCERNING FUEL RAIL LEAKAGE, DAIMLERCHRYSLER COMMENCED A RECALL (98V-184) OF APPROXIMATELY 722,600 VEHICLES TO ADDRESS ENGINE FUEL RAIL LEAKS THAT COULD LEAD TO A FIRE, INCLUDING THOSE VEHICLES CITED IN THE PETITION AND THE PETITIONER'S 1996 DODGE INTREPID.ON OCTOBER 7, 1998, NHTSA OPENED A RECALL QUERY INVESTIGATION (RQ98-018) TO EVALUATE THE ADEQUACY OF THE RECALL REMEDY.THAT INVESTIGATION WAS CLOSED ON JULY 8, 2002 WITHOUT REQUIRING FURTHER ACTION BY DAIMLERCHRYSLER.VERY RECENTLY, ON JUNE 9, 2004, NHTSA DENIED A PETITION (RP04-001) TO REOPEN RQ98-018 AFTER FINDING THAT THERE WAS NO NEW INFORMATION THAT WOULD INDICATE ANY BASIS FOR REOPENING IT.THIS IS STILL THE CURRENT POSITION OF NHTSA ON THIS ISSUE.CONCERNING BRAKE FLUID CONTAMINATION AND FRAME ALIGNMENT, A REVIEW OF NHTSA'S DATABASE SHOWS NO OTHER COMPLAINTS ON EITHER ONE OF THESE ISSUES ON THE VEHICLES CITED IN THE PETITION.

Service Brakes, Hydraulic:fluid

ON SEPTEMBER 5, 2004, MR. ROBERT GALENTY OF ISELIN, NJ, PETITIONED THE AGENCY TO CONDUCT DEFECT INVESTIGATIONS OF CERTAIN MODEL YEAR (MY) 1993-1997 VEHICLES PRODUCED BY DAIMLERCHRYSLER CORPORATION.HIS PETITION IDENTIFIED THREE ISSUES OF CONCERN: 1) FUEL LEAKING FROM THE FUEL INJECTOR RAILS; 2) BRAKE FLUID CONTAMINATION RESULTING IN BRAKE FAILURE; AND 3) SUSCEPTIBILITY OF THE VEHICLE FRAME TO DAMAGE WHILE THE VEHICLE IS BEING TOWED.MR. GALANTY ALLEGED THAT HIS 1996 DODGE INTREPID HAD EACH OF THESE THREE PROBLEMS.CONCERNING FUEL RAIL LEAKAGE, DAIMLERCHRYSLER COMMENCED A RECALL (98V-184) OF APPROXIMATELY 722,600 VEHICLES TO ADDRESS ENGINE FUEL RAIL LEAKS THAT COULD LEAD TO A FIRE, INCLUDING THOSE VEHICLES CITED IN THE PETITION AND THE PETITIONER'S 1996 DODGE INTREPID.ON OCTOBER 7, 1998, NHTSA OPENED A RECALL QUERY INVESTIGATION (RQ98-018) TO EVALUATE THE ADEQUACY OF THE RECALL REMEDY.THAT INVESTIGATION WAS CLOSED ON JULY 8, 2002 WITHOUT REQUIRING FURTHER ACTION BY DAIMLERCHRYSLER.VERY RECENTLY, ON JUNE 9, 2004, NHTSA DENIED A PETITION (RP04-001) TO REOPEN RQ98-018 AFTER FINDING THAT THERE WAS NO NEW INFORMATION THAT WOULD INDICATE ANY BASIS FOR REOPENING IT.THIS IS STILL THE CURRENT POSITION OF NHTSA ON THIS ISSUE.CONCERNING BRAKE FLUID CONTAMINATION AND FRAME ALIGNMENT, A REVIEW OF NHTSA'S DATABASE SHOWS NO OTHER COMPLAINTS ON EITHER ONE OF THESE ISSUES ON THE VEHICLES CITED IN THE PETITION.

Structure:frame And Members

ON SEPTEMBER 5, 2004, MR. ROBERT GALENTY OF ISELIN, NJ, PETITIONED THE AGENCY TO CONDUCT DEFECT INVESTIGATIONS OF CERTAIN MODEL YEAR (MY) 1993-1997 VEHICLES PRODUCED BY DAIMLERCHRYSLER CORPORATION.HIS PETITION IDENTIFIED THREE ISSUES OF CONCERN: 1) FUEL LEAKING FROM THE FUEL INJECTOR RAILS; 2) BRAKE FLUID CONTAMINATION RESULTING IN BRAKE FAILURE; AND 3) SUSCEPTIBILITY OF THE VEHICLE FRAME TO DAMAGE WHILE THE VEHICLE IS BEING TOWED.MR. GALANTY ALLEGED THAT HIS 1996 DODGE INTREPID HAD EACH OF THESE THREE PROBLEMS.CONCERNING FUEL RAIL LEAKAGE, DAIMLERCHRYSLER COMMENCED A RECALL (98V-184) OF APPROXIMATELY 722,600 VEHICLES TO ADDRESS ENGINE FUEL RAIL LEAKS THAT COULD LEAD TO A FIRE, INCLUDING THOSE VEHICLES CITED IN THE PETITION AND THE PETITIONER'S 1996 DODGE INTREPID.ON OCTOBER 7, 1998, NHTSA OPENED A RECALL QUERY INVESTIGATION (RQ98-018) TO EVALUATE THE ADEQUACY OF THE RECALL REMEDY.THAT INVESTIGATION WAS CLOSED ON JULY 8, 2002 WITHOUT REQUIRING FURTHER ACTION BY DAIMLERCHRYSLER.VERY RECENTLY, ON JUNE 9, 2004, NHTSA DENIED A PETITION (RP04-001) TO REOPEN RQ98-018 AFTER FINDING THAT THERE WAS NO NEW INFORMATION THAT WOULD INDICATE ANY BASIS FOR REOPENING IT.THIS IS STILL THE CURRENT POSITION OF NHTSA ON THIS ISSUE.CONCERNING BRAKE FLUID CONTAMINATION AND FRAME ALIGNMENT, A REVIEW OF NHTSA'S DATABASE SHOWS NO OTHER COMPLAINTS ON EITHER ONE OF THESE ISSUES ON THE VEHICLES CITED IN THE PETITION.

Fuel System, Gasoline:delivery:hoses, Lines/piping, And Fittings

NITRILE RUBBER SEALS USED IN THE FUEL RAIL ASSEMBLIES OF THE SUBJECT VEHICLES AT THE SUPPLY, RETURN, AND CROSSOVER TUBE FITTINGS, AND AT THE PRESSURE REGULATOR FAIL, RESULTING IN FUEL LEAKAGE IN THE ENGINE COMPARTMENT.ALSO, THE OUTLET (RIGHT) FUEL RAIL MAY LEAK FROM CRACKS AT CERTAIN MOLD GATES IN THE THERMOSET RAIL MATERIAL.CHRYSLER WILL RECALL THE SUBJECT VEHICLES AND STATED THAT IT INTENDS TO REPLACE THE O-RINGS WITH FLUOROCARBON O-RING HAVING GREATER HEAT RESISTANCE CAPABILITY AND ATTACH REINFORCEMENTS TO THE RAIL IN THE AREAS WHERE THE CRACKING CONCERN HAS BEEN KNOWN TO OCCUR MOST FREQUENTLY.RAILS THAT ARE ALREADY CRACKED WILL BE REPLACED BY NEW, REINFORCED RAILS.

Fuel System, Gasoline:fuel Injection System

NITRILE RUBBER SEALS USED IN THE FUEL RAIL ASSEMBLIES OF THE SUBJECT VEHICLES AT THE SUPPLY, RETURN, AND CROSSOVER TUBE FITTINGS, AND AT THE PRESSURE REGULATOR FAIL, RESULTING IN FUEL LEAKAGE IN THE ENGINE COMPARTMENT.ALSO, THE OUTLET (RIGHT) FUEL RAIL MAY LEAK FROM CRACKS AT CERTAIN MOLD GATES IN THE THERMOSET RAIL MATERIAL.CHRYSLER WILL RECALL THE SUBJECT VEHICLES AND STATED THAT IT INTENDS TO REPLACE THE O-RINGS WITH FLUOROCARBON O-RING HAVING GREATER HEAT RESISTANCE CAPABILITY AND ATTACH REINFORCEMENTS TO THE RAIL IN THE AREAS WHERE THE CRACKING CONCERN HAS BEEN KNOWN TO OCCUR MOST FREQUENTLY.RAILS THAT ARE ALREADY CRACKED WILL BE REPLACED BY NEW, REINFORCED RAILS.

Fuel System, Gasoline:fuel Injection System:fuel Rail

NITRILE RUBBER SEALS USED IN THE FUEL RAIL ASSEMBLIES OF THE SUBJECT VEHICLES AT THE SUPPLY, RETURN, AND CROSSOVER TUBE FITTINGS, AND AT THE PRESSURE REGULATOR FAIL, RESULTING IN FUEL LEAKAGE IN THE ENGINE COMPARTMENT.ALSO, THE OUTLET (RIGHT) FUEL RAIL MAY LEAK FROM CRACKS AT CERTAIN MOLD GATES IN THE THERMOSET RAIL MATERIAL.CHRYSLER WILL RECALL THE SUBJECT VEHICLES AND STATED THAT IT INTENDS TO REPLACE THE O-RINGS WITH FLUOROCARBON O-RING HAVING GREATER HEAT RESISTANCE CAPABILITY AND ATTACH REINFORCEMENTS TO THE RAIL IN THE AREAS WHERE THE CRACKING CONCERN HAS BEEN KNOWN TO OCCUR MOST FREQUENTLY.RAILS THAT ARE ALREADY CRACKED WILL BE REPLACED BY NEW, REINFORCED RAILS.